Fine gold 999,9 |
586 g |
+ Master alloy |
414 g A114/16 Y |
Colour |
green yellow |
Further information
Order-No. |
2620101108 |
Designation |
A114/16 Y , for 14K yellow gold |
Technical data
Melting range |
970°C - 940°C |
Density |
12,6 g/cm³ |
Hardness |
as cast: 170 HV |
Application |
jewellery casting and continuous casting as sheet, wire, tube |
Processing
Casting |
suitable for vacuum casting and centrifugal casting, as well as continuous casting of tube, strip and wire |
Casting temperature |
960°C - 1000°C |
Flask temp. |
580°C - 640°C |
Investment |
plaster bonded |
Quenching |
in 80°C hot water after 20 - 25minutes |
Working |
Material can be deformed max. 50%, then it must be annealed. Only roll a little at a time. Roll the same thickness several times if necessary. |
Heat treatment
Annealing |
600°C / 30 min, and then quench in hot water |
Hardening |
400°C - 440°C / 60 min, slow cool in air |
Brazing |
WIELAND brazing alloys 1421H (790°C), |
Flux |
Fluoron |
Pickling agent |
sulphuric acid (H2SO4) 10 % |