Fine gold 999,9 |
376 g |
+ Master alloy |
624 g A109/Y |
Colour |
yellow |
Further information
Order-No. |
2610100108 |
Designation |
A109/Y, for 9K yellow gold |
Technical data
Melting range |
830°C - 730°C |
Density |
10,9 g/cm³ |
Hardness |
as cast: 145 HV |
Application |
jewellery casting |
Processing
Casting |
suitable for vacuum casting and centrifugal casting |
Casting temperature |
970 °C - 1000°C |
Flask temp. |
600°C - 640°C |
Investment |
plaster bonded |
Quenching |
in 80°C hot water after 15 - 20 minutes |
Working |
Material can be deformed max. 50% then it must be annealed. Only roll a little at a time. Roll the same thickness several times if necessary. |
Heat treatment
Annealing |
650°C / 30 min, and then quench in hot water |
Hardening |
400°C - 440°C / 60 min, slow cool in air |
Brazing |
WIELAND brazing alloys 1010H (700°C), 1011M (660°C) |
Flux |
Fluoron |
Pickling agent |
sulphuric acid (H2SO4) 10 % |